• Scam Alert. Members are reminded to NOT send money to buy anything. Don't buy things remote and have it shipped - go get it yourself, pay in person, and take your equipment with you. Scammers have burned people on this forum. Urgency, secrecy, excuses, selling for friend, newish members, FUD, are RED FLAGS. A video conference call is not adequate assurance. Face to face interactions are required. Please report suspicions to the forum admins. Stay Safe - anyone can get scammed.
  • Several Regions have held meetups already, but others are being planned or are evaluating the interest. The Ontario GTA West area meetup is planned for Saturday April 26th at Greasemonkeys shop in Aylmer Ontario. If you are interested and haven’t signed up yet, click here! Arbutus has also explored interest in a Fraser Valley meetup but it seems members either missed his thread or had other plans. Let him know if you are interested in a meetup later in the year by posting here! Slowpoke is trying to pull together an Ottawa area meetup later this summer. No date has been selected yet, so let him know if you are interested here! We are not aware of any other meetups being planned this year. If you are interested in doing something in your area, let everyone know and make it happen! Meetups are a great way to make new machining friends and get hands on help in your area. Don’t be shy, sign up and come, or plan your own meetup!

Calgary- Delrin bushings

N

Neil B

Guest
I'm looking to get some delrin bushings machined for 2 carburetor throttle spindles. I would need a total of 4 bushings.

Each bushing is:
  • made from 9/16" nominal diameter delrin rod
  • has a 9/32" center hole
  • approximately 0.835″ in length
  • has a 0.59" long section cut to an OD of of 0.380" - 0.0385"
Here is a quick CAD drawing I made:

HAL6Wn8.png


If I am getting these made I might as well also have them pressed into the carb bodies and bored out/aligned.

I got the idea for this on a blog written by a gentleman from Maine. He outlines how he manufactures and installs the bushings in the link below.

It's quite a long post so I would suggest that once you are on his page, use ctrl + f to search for the following text "Delrin bushings that I use in Type HIF-6 carburetors". This will take you to the relevant section.

HIF-6 Rebuild

I have not taken this to a professional shop yet and I would ideally like it done this week or even this weekend. I can source the rod. I'm located in the SW but would be willing to travel to any part of the city.

Thank you in advance,
Neil
 
I decided to try printing said parts with my new 3D printer. Here in the photo you can see two with two more printing in the background. I think - think - they will be ok with gasoline due to the attached chart. The printing material is PETG. No guarantees though. I think they turned out as pretty good parts. I upped the density to 70% from the default 20%.

http://sevierlab.vet.cornell.edu/resources/Chemical-Resistance-Chart-Detail.pdf

@Neil B PM me and we can see if you want these parts.
 
Photos. So does the forum think this would be ok in an engine?
 

Attachments

  • 12A9D570-5C93-43FF-87CF-D3AE56358757.jpeg
    12A9D570-5C93-43FF-87CF-D3AE56358757.jpeg
    108.7 KB · Views: 0
  • D938EDA6-8269-462A-BD3F-9B5FAB79DA67.jpeg
    D938EDA6-8269-462A-BD3F-9B5FAB79DA67.jpeg
    95.8 KB · Views: 3
Well abs is very unstable in fuel. PLA resists gasoline for a little bit.You would need to print it out of nylon if you have any hope of it standing up to the gasoline. Looks good John, I like that you are always trying stuff,
 
This is not pla or abs. Its PETG so that might be better. Needs more research.
 

Attachments

  • 6BF6BB35-B71F-4763-B30A-5EDA9AEFA309.jpeg
    6BF6BB35-B71F-4763-B30A-5EDA9AEFA309.jpeg
    74.9 KB · Views: 0
  • image.jpg
    image.jpg
    92.7 KB · Views: 0
John, looks like you got your printer printing diameters accurately. Did you end up changing anything ?


Sent from my iPhone using Tapatalk
 
Odd - external diameters are fine - the internal ones are still out. I'm not sure why your clone is better. ???
 