• Scam Alert. Members are reminded to NOT send money to buy anything. Don't buy things remote and have it shipped - go get it yourself, pay in person, and take your equipment with you. Scammers have burned people on this forum. Urgency, secrecy, excuses, selling for friend, newish members, FUD, are RED FLAGS. A video conference call is not adequate assurance. Face to face interactions are required. Please report suspicions to the forum admins. Stay Safe - anyone can get scammed.
  • Several Regions have held meetups already, but others are being planned or are evaluating the interest. The Ontario GTA West area meetup is planned for Saturday April 26th at Greasemonkeys shop in Aylmer Ontario. If you are interested and haven’t signed up yet, click here! Arbutus has also explored interest in a Fraser Valley meetup but it seems members either missed his thread or had other plans. Let him know if you are interested in a meetup later in the year by posting here! Slowpoke is trying to pull together an Ottawa area meetup later this summer. No date has been selected yet, so let him know if you are interested here! We are not aware of any other meetups being planned this year. If you are interested in doing something in your area, let everyone know and make it happen! Meetups are a great way to make new machining friends and get hands on help in your area. Don’t be shy, sign up and come, or plan your own meetup!

Power Hammer Dies

Crosche

Super User
I am thinking about fabricating a pair of dies for my 25# Little Giant hammer. Currently I am thinking about making the dies from either 1045 or 4140....heat treated of course. The dies need to be hardend to between 42~46 HRC. Anyone have any insights on either of those materials?
 
Coincidental you mention this because I was looking for some kind of online tool that one could pick 2 alloys & show a comparative HT hardness/toughness overlay plot on common axis. If anyone has seen anything like this, I'd like to know. I could replicate in Excel but kind of pita. Anyways, hopefully this demonstrates the interplay between hardness, toughness & corresponding tempering temp. Your application may favor a certain combination or one over the other. And then of course there is machineability of the part itself if that's an issue.

4140
1635272979209.webp


O1 tool steel
1635273009429.webp
 
I made cold forging dies out of annealed 4140. Heat treat was done twice to a dark to medium cherry with no tempering. My dies were 2.5 inches thick so lots of material to absorb the after affects of the hit(100 tons).
 
2" x 2" 4140CR is what I am planning to make my dies from. My friend has a heat treating oven, so I should be able to get close to 48 HRC. Little Giant has a 2 part die system now that I am adapting to my machine.
 
That would work just fine - you can heat treat in the normal way and then temper to 48HRC by choosing the correct temperature. 4140 is pretty simple to heat treat, and is hard to mess up.
 